Fractographs

Low-Alloy Steel

M. Sherif and H. K. D. H. Bhadeshia

An Fe-0.1C-1.01Mn-0.24Si-0.76Cr-0.034Nb-0.037Al-0.0076N-0.0014O-0.002S-0.004P wt% steel, austentised at 870°C for 10 minutes and air cooled. The average cooling rate over the temperature range 800-500°C was 0.63°C s-1. Charpy tests were conducted at ambient temperature.






















The following fractographs are from the same steel, but heated 1000°C and immediately air cooled.