NUMBER PHASE STATUS MODEL 1 BCC_A2 NORMAL SUBLATTICE 2 CEMENTITE NORMAL SUBLATTICE 3 FCC_A1 ABSENT SUBLATTICE 4 HCP_A3 NORMAL SUBLATTICE 5 M7C3 NORMAL SUBLATTICE 6 M23C6 NORMAL SUBLATTICE 7 M6C NORMAL SUBLATTICE 8 MC_ETA NORMAL SUBLATTICE 9 LAVES_PHASE ABSENT SUBLATTICE 10 CNb ABSENT PURE SUBSTANCE 11 CTa ABSENT PURE SUBSTANCE 12 NNb ABSENT PURE SUBSTANCE 13 NTa ABSENT PURE SUBSTANCE 14 NV ABSENT PURE SUBSTANCE MULTIPHASE OPTION ? set w=100 ! MULTIPHASE OPTION ? set w(2)= 0.15 w(3)=0.3 w(4)=0.5 w(5)=0.2 w(6)=0.9 w(7)=2.25 ! MULTIPHASE OPTION ? li sys co ! NUMBER COMPONENT STATUS AMOUNT DELTA REF.P 1 Fe # TO BAL 1713.61 2 C NORMAL 12.4886 3 Si NORMAL 10.6817 4 Mn NORMAL 9.10117 5 Ni NORMAL 3.40774 6 Mo NORMAL 9.38086 7 Cr NORMAL 43.2726 8 V ABSENT undefined 9 W ABSENT undefined 10 Nb ABSENT undefined 11 Ta ABSENT undefined 12 N ABSENT undefined MULTIPHASE OPTION ? set temp 833 ! MULTIPHASE OPTION ? compute print brief print mol ! *** MULTIPHASE - Stage 1* Results *** Temperature = 833.0000 K Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.199001E+04 9.864249E-03 1.713610E+03 9.570000E+01 C -3.189247E+04 1.000415E-02 1.248855E+01 1.500000E-01 Si -1.700644E+05 2.168214E-11 1.068167E+01 3.000000E-01 Mn -6.385972E+04 9.900840E-05 9.101169E+00 5.000000E-01 Ni -7.106115E+04 3.500304E-05 3.407736E+00 2.000000E-01 Mo -5.041207E+04 6.900931E-04 9.380863E+00 9.000000E-01 Cr -4.595734E+04 1.312930E-03 4.327256E+01 2.250000E+00 Total 1.801943E+03 1.000000E+02 Gibbs Energy = -6.0316236846E+07 J Amount Phase Mole fraction of component within phase compnt moles Fe C Si 1.7415E+03 BCC_A2 0.9745999 0.0000028 0.0061338 5.9999E+01 M23C6 0.2706276 0.2068966 0.0000000 4.9158E-01 M6C 0.3119456 0.1428571 0.0000000 Mn Ni Mo 1.7415E+03 BCC_A2 0.0052161 0.0019567 0.0018243 5.9999E+01 M23C6 0.0002928 0.0000045 0.0991667 4.9158E-01 M6C 0.0000000 0.0000000 0.5167376 Cr 1.7415E+03 BCC_A2 0.0102664 5.9999E+01 M23C6 0.4230119 4.9158E-01 M6C 0.0284596 System Enthalpy = 2.8965958557E+07 J ------------------ MULTIPHASE OPTION ? li sys co ! NUMBER COMPONENT STATUS AMOUNT DELTA REF.P 1 Fe # TO BAL 1713.61 2 C NORMAL 12.4886 3 Si NORMAL 10.6817 4 Mn NORMAL 9.10117 5 Ni NORMAL 3.40774 6 Mo NORMAL 9.38086 7 Cr NORMAL 43.2726 8 V ABSENT undefined 9 W ABSENT undefined 10 Nb ABSENT undefined 11 Ta ABSENT undefined 12 N ABSENT undefined MULTIPHASE OPTION ? set w(2)=0.05 ! MULTIPHASE OPTION ? lis sys co ! NUMBER COMPONENT STATUS AMOUNT DELTA REF.P 1 Fe # TO BAL 1715.40 2 C NORMAL 4.16285 3 Si NORMAL 10.6817 4 Mn NORMAL 9.10117 5 Ni NORMAL 3.40774 6 Mo NORMAL 9.38086 7 Cr NORMAL 43.2726 8 V ABSENT undefined 9 W ABSENT undefined 10 Nb ABSENT undefined 11 Ta ABSENT undefined 12 N ABSENT undefined MULTIPHASE OPTION ? compute print brief print mol ! *** MULTIPHASE - Stage 1* Results *** Temperature = 833.0000 K Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.205678E+04 9.769617E-03 1.715401E+03 9.580000E+01 C -4.273251E+04 2.091487E-03 4.162851E+00 5.000000E-02 Si -1.699486E+05 2.204751E-11 1.068167E+01 3.000000E-01 Mn -6.417241E+04 9.463782E-05 9.101169E+00 5.000000E-01 Ni -7.138179E+04 3.341950E-05 3.407736E+00 2.000000E-01 Mo -4.764414E+04 1.029131E-03 9.380863E+00 9.000000E-01 Cr -4.169509E+04 2.429441E-03 4.327256E+01 2.250000E+00 Total 1.795408E+03 1.000000E+02 Gibbs Energy = -6.0062495874E+07 J Amount Phase Mole fraction of component within phase compnt moles Fe C Si 1.7735E+03 BCC_A2 0.9645342 0.0000008 0.0060228 1.6171E+01 M23C6 0.1878213 0.2068966 0.0000000 5.7093E+00 M6C 0.3040961 0.1428571 0.0000000 Mn Ni Mo 1.7735E+03 BCC_A2 0.0051304 0.0019214 0.0027165 1.6171E+01 M23C6 0.0001447 0.0000027 0.1002650 5.7093E+00 M6C 0.0000000 0.0000000 0.5152370 Cr 1.7735E+03 BCC_A2 0.0196739 1.6171E+01 M23C6 0.5048697 5.7093E+00 M6C 0.0378098