Calculations to show that Widmanstaetten ferrite forms below the T_0 temperature in Fe-7.4Cr-1.8Ni wt% alloy studied by Ricks, Bee and Howell, Metallurgical Transactions A. 1981 Sep 1;12(9):1587-94. Last login: Mon Apr 27 06:00:19 on console user-7:~ harshadbhadeshia$ ssh hkdb@ptlin4.msm.cam.ac.uk Password: Last login: Wed Apr 15 14:10:41 2020 from user-6.msm.private.cam.ac.uk hkdb@ptlin4:~$ mtdata ******************************* * USING DEFAULT MTSIGNON FILE * ******************************* ┌───────────────────────────────────────────────────────────────────────────┐ │ ▒▒ ▒▒ ▒▒▒▒▒▒▒▒▒ ▒▒▒▒▒▒▒ ▒▒▒ ▒▒▒▒▒▒▒▒▒ ▒▒▒ │ │ ▒▒▒ ▒▒▒ ▒▒▒▒▒▒▒▒▒ ▒▒ ▒▒ ▒▒ ▒▒ ▒▒▒▒▒▒▒▒▒ ▒▒ ▒▒ │ │ ▒▒ ▒ ▒ ▒▒ ▒▒▒ ▒▒ ▒▒▒ ▒▒ ▒▒ ▒▒▒ ▒▒ ▒▒ │ │ ▒▒ ▒ ▒▒ ▒▒▒ ▒▒ ▒▒▒ ▒▒▒▒▒▒▒▒▒ ▒▒▒ ▒▒▒▒▒▒▒▒▒ │ │ ▒▒ ▒▒ ▒▒▒ ▒▒ ▒▒ ▒▒ ▒▒ ▒▒▒ ▒▒ ▒▒ │ │ ▒▒ ▒▒ ▒▒▒ ▒▒▒▒▒▒▒ ▒▒ ▒▒ ▒▒▒ ▒▒ ▒▒ │ └───────────────────────────────────────────────────────────────────────────┘ - THERMODYNAMICS AND PROCESS MODELLING GROUP - - NPL MATERIALS CENTRE - - NATIONAL PHYSICAL LABORATORY - Authorised for use by Dr H K D H Bhadeshia at University of Cambridge under the terms and conditions of NPL 79/199-3 ┌───────────────────────────────┐ │ VERSION 4.73 FOR LNX RH 7.3 │ │ 2002-11-15 │ └───────────────────────────────┘ ******************************* * USING DEFAULT MTCONFIG FILE * ******************************* 19 of 32 DATABASES ARE AVAILABLE WHICH MODULE ? multiphase MULTIPHASE OPTION ? define system "Fe,Cr,Ni" ! SEARCHING FOR SYSTEM Fe,Cr,Ni SEARCHING DATABASE(S) : sgte_sol - SGTE Solution Database v4.2 6/12/2006 SIMPLIFIED MODEL USED FOR PHASE CR3SI_A15:3:1 SIMPLIFIED MODEL USED FOR PHASE CRSI2:1:2 SIMPLIFIED MODEL USED FOR PHASE BCC_A2:1:3 SIMPLIFIED MODEL USED FOR PHASE FCC_A1:1:1 SIMPLIFIED MODEL USED FOR PHASE CBCC_A12:1:1 SIMPLIFIED MODEL USED FOR PHASE CUB_A13:1:1 SIMPLIFIED MODEL USED FOR PHASE HCP_A3:1:.5 SIMPLIFIED MODEL USED FOR PHASE HCP_ZN:1:.5 SIMPLIFIED MODEL USED FOR PHASE FE2U:2:1 SIMPLIFIED MODEL USED FOR PHASE FESB:1:1 SIMPLIFIED MODEL USED FOR PHASE FEU6:1:6 SIMPLIFIED MODEL USED FOR PHASE FEUZR_DELTA:1:2 SIMPLIFIED MODEL USED FOR PHASE FEZN4:.25:.75 SIMPLIFIED MODEL USED FOR PHASE FEZN_DELTA:.125:.875 SIMPLIFIED MODEL USED FOR PHASE FEZN_GAMMA_D82:.3:.7 SIMPLIFIED MODEL USED FOR PHASE FEZN_ZETA:.072:0.928 SIMPLIFIED MODEL USED FOR PHASE FEZR2:1:2 SIMPLIFIED MODEL USED FOR PHASE FEZR3:1:3 SIMPLIFIED MODEL USED FOR PHASE B2_BCC:1:1 SIMPLIFIED MODEL USED FOR PHASE NI3MOTA:.75:.25 SIMPLIFIED MODEL USED FOR PHASE NI3NB:3:1 SIMPLIFIED MODEL USED FOR PHASE NI10ZR7:.575:.425 SIMPLIFIED MODEL USED FOR PHASE NI3ZR:.75:.25 SIMPLIFIED MODEL USED FOR PHASE NI5ZR:.833:.167 SIMPLIFIED MODEL USED FOR PHASE NI3TI:.75:.25:.5 ERROR: NO DATA FOUND FOR UNARY Cr:Fe ERROR: NO DATA FOUND FOR UNARY Fe:Cr ERROR: NO DATA FOUND FOR UNARY Fe:Ni ERROR: NO DATA FOUND FOR UNARY Ni:Fe ERROR: NO DATA FOR BINARY INTERACTION Cr:Cr,Fe ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Cr ERROR: NO DATA FOR BINARY INTERACTION Cr:Fe,Ni ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Fe ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni:Fe ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Ni ERROR: NO DATA FOR BINARY INTERACTION Fe:Cr,Fe ERROR: NO DATA FOR BINARY INTERACTION Fe:Cr,Ni ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni:Cr ERROR: NO DATA FOR BINARY INTERACTION Fe:Fe,Ni ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni:Fe ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni:Ni ERROR: NO DATA FOR BINARY INTERACTION Ni:Cr,Fe ERROR: NO DATA FOR BINARY INTERACTION Ni:Fe,Ni ERROR: NO DATA FOUND FOR UNARY Cr:Fe ERROR: NO DATA FOUND FOR UNARY Fe:Cr ERROR: NO DATA FOUND FOR UNARY Fe:Ni ERROR: NO DATA FOUND FOR UNARY Ni:Fe ERROR: NO DATA FOR BINARY INTERACTION Cr:Cr,Fe ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Cr ERROR: NO DATA FOR BINARY INTERACTION Cr:Fe,Ni ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Fe ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni:Fe ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Ni ERROR: NO DATA FOR BINARY INTERACTION Fe:Cr,Fe ERROR: NO DATA FOR BINARY INTERACTION Fe:Cr,Ni ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni:Cr ERROR: NO DATA FOR BINARY INTERACTION Fe:Fe,Ni ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni:Fe ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni:Ni ERROR: NO DATA FOR BINARY INTERACTION Ni:Cr,Fe ERROR: NO DATA FOR BINARY INTERACTION Ni:Fe,Ni ERROR: NO DATA FOUND FOR UNARY Cr:Ni ERROR: NO DATA FOUND FOR UNARY Ni:Cr ERROR: NO DATA FOR BINARY INTERACTION Cr:Cr,Ni ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni:Cr ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni:Ni ERROR: NO DATA FOR BINARY INTERACTION Ni:Cr,Ni ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni MISSING DATA ASSUMED ZERO: PHASE MAGNETIC BUT NO MAGNETIC DATA FOR Fe MISSING DATA ASSUMED ZERO: PHASE MAGNETIC BUT NO MAGNETIC DATA FOR Ni ERROR: NO DATA FOUND FOR UNARY Cr:Fe:Va ERROR: NO DATA FOUND FOR UNARY Cr:Ni:Va ERROR: NO DATA FOUND FOR UNARY Fe:Cr:Va ERROR: NO DATA FOUND FOR UNARY Fe:Ni:Va ERROR: NO DATA FOUND FOR UNARY Ni:Cr:Va ERROR: NO DATA FOUND FOR UNARY Ni:Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Cr:Cr,Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Cr:Cr,Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Cr:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni:Cr:Va ERROR: NO DATA FOR BINARY INTERACTION Cr:Fe,Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni:Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni:Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Fe:Cr,Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Fe:Cr,Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni:Cr:Va ERROR: NO DATA FOR BINARY INTERACTION Fe:Fe,Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni:Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni:Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Ni:Cr,Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Ni:Cr,Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Ni:Fe,Ni:Va ERROR: NO DATA FOUND FOR UNARY Cr:Fe:Va ERROR: NO DATA FOUND FOR UNARY Cr:Ni:Va ERROR: NO DATA FOUND FOR UNARY Fe:Cr:Va ERROR: NO DATA FOUND FOR UNARY Ni:Cr:Va ERROR: NO DATA FOR BINARY INTERACTION Cr:Cr,Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Cr:Cr,Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Cr:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni:Cr:Va ERROR: NO DATA FOR BINARY INTERACTION Cr:Fe,Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni:Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Fe:Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Cr,Ni:Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Fe:Cr,Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Fe:Cr,Ni:Va ERROR: NO DATA FOR BINARY INTERACTION Fe,Ni:Cr:Va ERROR: NO DATA FOR BINARY INTERACTION Ni:Cr,Fe:Va ERROR: NO DATA FOR BINARY INTERACTION Ni:Cr,Ni:Va ****** 7 PHASES IDENTIFIED WITH INCORRECT OR MISSING DATA ****** PHASE: LAVES_C14:2:1 ERROR: Missing data for unary(s) PHASE: LAVES_C15:2:1 ERROR: Missing data for unary(s) PHASE: LAVES_C36:2:1 ERROR: Missing data for unary(s) PHASE: CBCC_A12 ERROR: Missing data for binary interaction(s) PHASE: CUB_A13 ERROR: Missing data for binary interaction(s) PHASE: BCC_B2:.5:.5:3 ERROR: Missing data for unary(s) PHASE: FCC_L12:.75:.25:1 ERROR: Missing data for unary(s) ****** GOOD DATAFILE CREATED (but missing/inconsistent data) ****** **************************************************** * FOR MISSING INTERACTION DATA SEE FILE misbin.dbl * **************************************************** Date and time of run 27-APR-2020 10:21:23 * DATAFILE = /mnt/bart/users/hkdb/def.mpi - CREATED 10:21:23 27-APR-2020 * SYSTEM = Fe,Cr,Ni, * NUMBER OF PHASES = 38 * NUMBER OF SPECIES = 90 * ******************************** * UNASSESSED OR INCORRECT DATA * ******************************** ************************************* * WARNING/ERRORS HAVE BEEN DETECTED * ************************************* 5 Warnings: UNASSESSED DATA - Missing data for unary(s) 2 Warnings: UNASSESSED DATA - Missing data for binary(s) MULTIPHASE OPTION ? lis sys ph ! NUMBER PHASE STATUS MODEL 1 LIQUID NORMAL REDLICH-KISTER 2 CR3SI_A15 NORMAL PURE SUBSTANCE 3 CRSI2 NORMAL PURE SUBSTANCE 4 LAVES_C14 ABSENT SUBLATTICE 5 LAVES_C15 ABSENT SUBLATTICE 6 LAVES_C36 ABSENT SUBLATTICE 7 CHI_A12 NORMAL SUBLATTICE 8 HIGH_SIGMA NORMAL SUBLATTICE 9 SIGMA NORMAL SUBLATTICE 10 BCC_A2 1 M-G REDLICH-KISTER 11 FCC_A1 1 M-G REDLICH-KISTER 12 CBCC_A12 ABSENT REDLICH-KISTER 13 CUB_A13 ABSENT REDLICH-KISTER 14 HCP_A3 NORMAL REDLICH-KISTER 15 HCP_ZN NORMAL PURE SUBSTANCE 16 BCC_B2 ABSENT CHEMICAL ORDERING(C) 17 FCC_L12 ABSENT CHEMICAL ORDERING 18 AL5FE4 NORMAL PURE SUBSTANCE 19 ORTHORHOMBIC_A20 NORMAL PURE SUBSTANCE 20 TETRAGONAL_U NORMAL PURE SUBSTANCE 21 FE2U NORMAL PURE SUBSTANCE >>>>> Type return for more, Q to quit paging : Q 22 FESB NORMAL PURE SUBSTANCE 23 FEU6 NORMAL PURE SUBSTANCE 24 FEUZR_DELTA NORMAL PURE SUBSTANCE 25 FEZN4 NORMAL PURE SUBSTANCE 26 FEZN_DELTA NORMAL PURE SUBSTANCE 27 FEZN_GAMMA_D82 NORMAL PURE SUBSTANCE 28 FEZN_ZETA NORMAL PURE SUBSTANCE 29 FEZR2 NORMAL PURE SUBSTANCE 30 FEZR3 NORMAL PURE SUBSTANCE 31 FE4N NORMAL SUBLATTICE 32 B2_BCC NORMAL REDLICH-KISTER 33 NI3MOTA NORMAL PURE SUBSTANCE 34 NI3NB NORMAL PURE SUBSTANCE 35 NI10ZR7 NORMAL PURE SUBSTANCE 36 NI3ZR NORMAL PURE SUBSTANCE 37 NI5ZR NORMAL PURE SUBSTANCE 38 NI3TI NORMAL PURE SUBSTANCE MULTIPHASE OPTION ? cl abs p(*) ! MULTIPHASE OPTION ? cl normal p(10),p(11) ! MULTIPHASE OPTION ? lis sys ph ! NUMBER PHASE STATUS MODEL 1 LIQUID ABSENT REDLICH-KISTER 2 CR3SI_A15 ABSENT PURE SUBSTANCE 3 CRSI2 ABSENT PURE SUBSTANCE 4 LAVES_C14 ABSENT SUBLATTICE 5 LAVES_C15 ABSENT SUBLATTICE 6 LAVES_C36 ABSENT SUBLATTICE 7 CHI_A12 ABSENT SUBLATTICE 8 HIGH_SIGMA ABSENT SUBLATTICE 9 SIGMA ABSENT SUBLATTICE 10 BCC_A2 1 M-G REDLICH-KISTER 11 FCC_A1 1 M-G REDLICH-KISTER 12 CBCC_A12 ABSENT REDLICH-KISTER 13 CUB_A13 ABSENT REDLICH-KISTER 14 HCP_A3 ABSENT REDLICH-KISTER 15 HCP_ZN ABSENT PURE SUBSTANCE 16 BCC_B2 ABSENT CHEMICAL ORDERING(C) 17 FCC_L12 ABSENT CHEMICAL ORDERING 18 AL5FE4 ABSENT PURE SUBSTANCE 19 ORTHORHOMBIC_A20 ABSENT PURE SUBSTANCE 20 TETRAGONAL_U ABSENT PURE SUBSTANCE 21 FE2U ABSENT PURE SUBSTANCE >>>>> Type return for more, Q to quit paging : 22 FESB ABSENT PURE SUBSTANCE 23 FEU6 ABSENT PURE SUBSTANCE 24 FEUZR_DELTA ABSENT PURE SUBSTANCE 25 FEZN4 ABSENT PURE SUBSTANCE 26 FEZN_DELTA ABSENT PURE SUBSTANCE 27 FEZN_GAMMA_D82 ABSENT PURE SUBSTANCE 28 FEZN_ZETA ABSENT PURE SUBSTANCE 29 FEZR2 ABSENT PURE SUBSTANCE 30 FEZR3 ABSENT PURE SUBSTANCE 31 FE4N ABSENT SUBLATTICE 32 B2_BCC ABSENT REDLICH-KISTER 33 NI3MOTA ABSENT PURE SUBSTANCE 34 NI3NB ABSENT PURE SUBSTANCE 35 NI10ZR7 ABSENT PURE SUBSTANCE 36 NI3ZR ABSENT PURE SUBSTANCE 37 NI5ZR ABSENT PURE SUBSTANCE 38 NI3TI ABSENT PURE SUBSTANCE MULTIPHASE OPTION ? lis sys co ! NUMBER COMPONENT STATUS AMOUNT DELTA REF.P 1 Fe NORMAL undefined 2 Cr NORMAL undefined 3 Ni NORMAL undefined MULTIPHASE OPTION ? set w 100 ! MULTIPHASE OPTION ? set w(2) 7.4 ! MULTIPHASE OPTION ? set w(3) 1.8 ! MULTIPHASE OPTION ? set w(1) undefined ! MULTIPHASE OPTION ? step temp 873 923 10 ! MULTIPHASE OPTION ? comp pr br pr weight ! NUMBER OF STEPS = 6 873.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 873.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.482400E+04 8.249180E-03 1.625871E+03 9.080000E+01 Cr -3.698174E+04 6.127862E-03 1.423186E+02 7.400000E+00 Ni -6.177775E+04 2.012400E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.3776707356E+07 J System Enthalpy = 3.6360752295E+07 J 883.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 883.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.544001E+04 8.008815E-03 1.625871E+03 9.080000E+01 Cr -3.781252E+04 5.797268E-03 1.423186E+02 7.400000E+00 Ni -6.280152E+04 1.927589E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.4928234005E+07 J System Enthalpy = 3.7147412490E+07 J 893.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 893.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.606109E+04 7.775279E-03 1.625871E+03 9.080000E+01 Cr -3.864829E+04 5.487640E-03 1.423186E+02 7.400000E+00 Ni -6.383169E+04 1.846543E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.6088739958E+07 J System Enthalpy = 3.7946611331E+07 J 903.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 903.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.668655E+04 7.549106E-03 1.625871E+03 9.080000E+01 Cr -3.948911E+04 5.197373E-03 1.423186E+02 7.400000E+00 Ni -6.486836E+04 1.769053E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.7258268541E+07 J System Enthalpy = 3.8758979371E+07 J 913.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 913.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.731843E+04 7.328046E-03 1.625871E+03 9.080000E+01 Cr -4.033533E+04 4.924808E-03 1.423186E+02 7.400000E+00 Ni -6.591168E+04 1.694922E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.8436869411E+07 J System Enthalpy = 3.9585203718E+07 J 923.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 923.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.795456E+04 7.114109E-03 1.625871E+03 9.080000E+01 Cr -4.118710E+04 4.668621E-03 1.423186E+02 7.400000E+00 Ni -6.696179E+04 1.623968E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.9624599002E+07 J System Enthalpy = 4.0426034230E+07 J MULTIPHASE OPTION ? ls abs p(10) ! LS KEYWORD NOT RECOGNISED MULTIPHASE OPTION ? cl abs p(10) ! MULTIPHASE OPTION ? comp pr br pr weight ! NUMBER OF STEPS = 6 873.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 873.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.399524E+04 9.246930E-03 1.625871E+03 9.080000E+01 Cr -3.795373E+04 5.359856E-03 1.423186E+02 7.400000E+00 Ni -6.911601E+04 7.322371E-05 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 FCC_A1 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.2793142396E+07 J System Enthalpy = 4.4707029536E+07 J 883.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 883.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.466648E+04 8.898679E-03 1.625871E+03 9.080000E+01 Cr -3.874891E+04 5.103078E-03 1.423186E+02 7.400000E+00 Ni -7.009622E+04 7.136764E-05 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 FCC_A1 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.4027733204E+07 J System Enthalpy = 4.5268640554E+07 J 893.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 893.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.534128E+04 8.566808E-03 1.625871E+03 9.080000E+01 Cr -3.954750E+04 4.861713E-03 1.423186E+02 7.400000E+00 Ni -7.107989E+04 6.956611E-05 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 FCC_A1 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.5268693470E+07 J System Enthalpy = 4.5831858059E+07 J 903.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 903.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.601961E+04 8.250388E-03 1.625871E+03 9.080000E+01 Cr -4.034947E+04 4.634646E-03 1.423186E+02 7.400000E+00 Ni -7.206701E+04 6.781736E-05 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 FCC_A1 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.6515969861E+07 J System Enthalpy = 4.6396682908E+07 J 913.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 913.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.670142E+04 7.948548E-03 1.625871E+03 9.080000E+01 Cr -4.115481E+04 4.420857E-03 1.423186E+02 7.400000E+00 Ni -7.305754E+04 6.611970E-05 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 FCC_A1 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.7769510233E+07 J System Enthalpy = 4.6963116094E+07 J 923.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 923.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.738670E+04 7.660479E-03 1.625871E+03 9.080000E+01 Cr -4.196349E+04 4.219409E-03 1.423186E+02 7.400000E+00 Ni -7.405146E+04 6.447148E-05 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 FCC_A1 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.9029263597E+07 J System Enthalpy = 4.7531158714E+07 J MULTIPHASE OPTION ? cls normal p(10) ! CLS KEYWORD NOT RECOGNISED MULTIPHASE OPTION ? cl normal p(10) ! MULTIPHASE OPTION ? cl abs p(11) ! MULTIPHASE OPTION ? comp pr br pr weight ! NUMBER OF STEPS = 6 873.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 873.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.482369E+04 8.249536E-03 1.625871E+03 9.080000E+01 Cr -3.698174E+04 6.127863E-03 1.423186E+02 7.400000E+00 Ni -6.177776E+04 2.012400E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.3776707356E+07 J System Enthalpy = 3.6360752296E+07 J 883.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 883.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.543991E+04 8.008920E-03 1.625871E+03 9.080000E+01 Cr -3.781252E+04 5.797268E-03 1.423186E+02 7.400000E+00 Ni -6.280152E+04 1.927589E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.4928234005E+07 J System Enthalpy = 3.7147412491E+07 J 893.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 893.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.606109E+04 7.775277E-03 1.625871E+03 9.080000E+01 Cr -3.864829E+04 5.487640E-03 1.423186E+02 7.400000E+00 Ni -6.383169E+04 1.846543E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.6088739958E+07 J System Enthalpy = 3.7946611332E+07 J 903.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 903.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.668726E+04 7.548388E-03 1.625871E+03 9.080000E+01 Cr -3.948911E+04 5.197373E-03 1.423186E+02 7.400000E+00 Ni -6.486836E+04 1.769053E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.7258268541E+07 J System Enthalpy = 3.8758979371E+07 J 913.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 913.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.731844E+04 7.328041E-03 1.625871E+03 9.080000E+01 Cr -4.033504E+04 4.925001E-03 1.423186E+02 7.400000E+00 Ni -6.591168E+04 1.694922E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.8436869411E+07 J System Enthalpy = 3.9585203719E+07 J 923.000 *** MULTIPHASE - Stage 1* Results *** Temperature = 923.0000 K Fixed pressure = 1.013250E+05 Pa, 1.000000E+00 atm Component Ref.Phase Chem.Pot. Activity Amount/mol Mass/kg Fe -3.795465E+04 7.114028E-03 1.625871E+03 9.080000E+01 Cr -4.118617E+04 4.669187E-03 1.423186E+02 7.400000E+00 Ni -6.696179E+04 1.623968E-04 3.066962E+01 1.800000E+00 Total 1.798859E+03 1.000000E+02 Mass/kg Phase Mass fraction of component within phase Fe Cr Ni 1.0000E+02 BCC_A2 0.9080000 0.0740000 0.0180000 Gibbs Energy = -6.9624599002E+07 J System Enthalpy = 4.0426034230E+07 J MULTIPHASE OPTION ?