Austempered Ductile Cast Iron (ADI)

Miguel Angel Yescas-Gonzalez and H. K. D. H. Bhadeshia

adi adi
Austenitised at 950°C, austempered at 400°C for 52 min Austenitised at 950°C, austempered at 400°C for 52 min
 
adi adi
Austenitised at 950°C, austempered at 350°C for 64 min Austenitised at 950°C, austempered at 350°C for 64 min
 
adi
Austenitised at 950°C, austempered at 350°C for 64 min


adi adi
Austenitised at 950°C, austempered at 300°C for 63 min Austenitised at 950°C, austempered at 300°C for 63 min
adi adi
Austenitised at 950°C, austempered at 250°C for 50 min Austenitised at 950°C, austempered at 250°C for 50 min