![Slide1](sp9-Thumbnails/0.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 3 days. |
![Slide2](sp9-Thumbnails/1.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 3 days. |
![Slide1_1](sp9-Thumbnails/2.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 4 days. |
![Slide2_1](sp9-Thumbnails/3.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 4 days. |
![Slide3](sp9-Thumbnails/4.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 4 days. |
![Slide4](sp9-Thumbnails/5.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 4 days. |
![Slide5](sp9-Thumbnails/6.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 4 days. |
![Slide6](sp9-Thumbnails/7.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 4 days. |
![Slide7](sp9-Thumbnails/8.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 4 days. |
![Slide1_2](sp9-Thumbnails/9.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide10](sp9-Thumbnails/10.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide11](sp9-Thumbnails/11.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide12](sp9-Thumbnails/12.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide13](sp9-Thumbnails/13.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide14](sp9-Thumbnails/14.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide15](sp9-Thumbnails/15.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide16](sp9-Thumbnails/16.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide2_2](sp9-Thumbnails/17.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide3_1](sp9-Thumbnails/18.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide4_1](sp9-Thumbnails/19.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide5_1](sp9-Thumbnails/20.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide6_1](sp9-Thumbnails/21.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide7_1](sp9-Thumbnails/22.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide8](sp9-Thumbnails/23.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide9](sp9-Thumbnails/24.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 200°C for 9 days. |
![Slide1_3](sp9-Thumbnails/25.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 250°C for 1 day. |
![Slide2_3](sp9-Thumbnails/26.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 250°C for 1 day. |
![Slide3_2](sp9-Thumbnails/27.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 250°C for 1 day. |
![Slide4_2](sp9-Thumbnails/28.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 250°C for 1 day. |
![Slide5_2](sp9-Thumbnails/29.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 250°C for 1 day. |
![Slide6_2](sp9-Thumbnails/30.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 250°C for 1 day. |
![Slide7_2](sp9-Thumbnails/31.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 250°C for 1 day. |
![Slide8_1](sp9-Thumbnails/32.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 250°C for 1 day. |
![Slide1_4](sp9-Thumbnails/33.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide10_1](sp9-Thumbnails/34.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide11_1](sp9-Thumbnails/35.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide12_1](sp9-Thumbnails/36.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide2_4](sp9-Thumbnails/37.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide3_3](sp9-Thumbnails/38.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide4_3](sp9-Thumbnails/39.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide5_3](sp9-Thumbnails/40.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide6_3](sp9-Thumbnails/41.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide7_3](sp9-Thumbnails/42.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide8_2](sp9-Thumbnails/43.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |
![Slide9_1](sp9-Thumbnails/44.jpg)
Fe-0.83C-1.57Si-1.98Mn-0.24Mo-1.02Cr-1.54Co wt% Austenitised at 900°C for 30 min. isothermally transformed at 300°C for 1 day. |