The recrystallisation behaviour of PM2000 oxide dispersion strengthened ferritic alloy has been investigated for samples which were cold deformed after extrusion. The evolution of the recrystallisation temperature TR, defined as the minimum temperature at which the sample begins to recrystallise, has been studied in detail as a function of the level of deformation. The microstructure was characterised using transmission electron and optical microscopy, together with microhardness measurements. The results can be interpreted if it is assumed that anything which makes the microstructure heterogeneous, stimulates recrystallisation. In this sense, larger strain gradients lead to more refined and more isotropic grain structures. The way in which these results can be exploited for commercial applications are discussed.
21st Riso International Symposium on Materials Science, eds N. Hansen, X. Huang, D. Juul Jensen, E. M. Lauridsen, T. Leffers, W. Pantleon, T. J. Sabin and J. A. Wert, published by Riso National Laboratory, Denmark, 2000, pp. 277-282.
En este trabajo se ha estudiado el comportamiento durante la recristalización de la aleación de base hierro refozada con particulas dispersas PM2000, en muestras que han sido deformadas en frio después de la extrusión. La evolución de TR, la mínima temperatura para la cual la muestra empieza a recristalizar, en función del nivel de deformación, ha sido cuidadosamente deteminada. Asi mismo, se ha caracterizado la microestrucutura resusltante con la ayuda de microscopía electronica de transmisión, óptica y medidas de microdureza. La interpretación de los resultados permite concluir que cualquier fenomeno que introduzca heterogeneidades en el material, estimula la recristalización. En este sentido, grandes gradientes de deformación producen un estructura de grano más fina e isotrópica, permitiendo mejores resultados desde un punto de vista de aplicación industrial.
21st Riso International Symposium on Materials Science, eds N. Hansen, X. Huang, D. Juul Jensen, E. M. Lauridsen, T. Leffers, W. Pantleon, T. J. Sabin and J. A. Wert, published by Riso National Laboratory, Denmark, 2000, pp. 277-282.
|
|
|
| Superalloys | Titanium | Bainite | Martensite | Widmanstätten ferrite |
| Cast iron | Welding | Allotriomorphic ferrite | Movies | Slides |
| Neural Networks | Creep | Mechanicallly Alloyed | Theses | Retained Austenite |
|
|
|
| PT Group Home | Materials Algorithms |
|
|