Designing Low-Temperature, Low-Carbon Bainite: Metallography of Fe-0.202C-2.50Mn-6.74Ni wt%

Hong-Seok Yang and H. K. D. H. Bhadeshia

100
Quenched, fully martensitic		 100 (2)
Quenched, fully martensitic		 632_M_1001
Quenched, fully martensitic
632_M_2001
Quenched, fully martensitic		 200 (2)
Quenched, fully martensitic		 200
Quenched, fully martensitic
500(8)
Quenched, fully martensitic		 500(9)
Quenched, fully martensitic		 500(3)
Quenched, fully martensitic
500(10)
Quenched, fully martensitic		 500(4)
Quenched, fully martensitic		 500(7)
Quenched, fully martensitic
500(11)
Quenched, fully martensitic		 632_M_5001
Quenched, fully martensitic		 632_M_5003
Quenched, fully martensitic
632_M_5002
Quenched, fully martensitic		 500 (4)
Quenched, fully martensitic		 500 (5)
Quenched, fully martensitic
500 (3)
Quenched, fully martensitic		 500 (1)
Quenched, fully martensitic		 500 (2)
Quenched, fully martensitic
500 (6)
Quenched, fully martensitic		 1000(4)
Quenched, fully martensitic		 1000(6)
Quenched, fully martensitic
1000(5)
Quenched, fully martensitic		 1000(7)
Quenched, fully martensitic		 1000(3)
Quenched, fully martensitic
1000 (6)
Quenched, fully martensitic		 1000 (11)
Quenched, fully martensitic		 1000
Quenched, fully martensitic
1000 (8)
Quenched, fully martensitic		 1000 (2)
Quenched, fully martensitic		 1000 (4)
Quenched, fully martensitic
1000 (10)
Quenched, fully martensitic		 1000 (9)
Quenched, fully martensitic		 1000 (7)
Quenched, fully martensitic
1000 (5)
Quenched, fully martensitic		 632_M_5004
Quenched, fully martensitic		 632_M_5002
Quenched, fully martensitic
632_M_5001
Quenched, fully martensitic		 632_M_5003
Quenched, fully martensitic		 653_M_2001
Quenched, fully martensitic
1004
Isothermally transformed at 310C, fully martensitic		 1001
Isothermally transformed at 310C, fully martensitic		 1001
Isothermally transformed at 310C, fully martensitic
2001
Isothermally transformed at 310C, fully martensitic		 2001
Isothermally transformed at 310C, fully martensitic		 2002
Isothermally transformed at 310C, fully martensitic
2003
Isothermally transformed at 310C, fully martensitic		 5001
Isothermally transformed at 310C, fully martensitic		 5004
Isothermally transformed at 310C, fully martensitic
5002
Isothermally transformed at 310C, fully martensitic		 5003
Isothermally transformed at 310C, fully martensitic		 5005
Isothermally transformed at 310C, fully martensitic
5001
Isothermally transformed at 310C, fully martensitic		 5002
Isothermally transformed at 310C, fully martensitic		 5005
Isothermally transformed at 310C, fully martensitic
5004
Isothermally transformed at 310C, fully martensitic		 5007
Isothermally transformed at 310C, fully martensitic		 5003
Isothermally transformed at 310C, fully martensitic
5006
Isothermally transformed at 310C, fully martensitic		 10001
Isothermally transformed at 310C, fully martensitic		 10002
Isothermally transformed at 310C, fully martensitic
10003
Isothermally transformed at 310C, fully martensitic		 10002
Isothermally transformed at 310C, fully martensitic		 10005
Isothermally transformed at 310C, fully martensitic
10004
Isothermally transformed at 310C, fully martensitic		 10001
Isothermally transformed at 310C, fully martensitic		 1001
Isothermally transformed at 300C, fully martensitic
2001
Isothermally transformed at 300C, fully martensitic		 2001
Isothermally transformed at 300C, fully martensitic		 5001
Isothermally transformed at 300C, fully martensitic
5004
Isothermally transformed at 300C, fully martensitic		 5003
Isothermally transformed at 300C, fully martensitic		 5002
Isothermally transformed at 300C, fully martensitic
5005
Isothermally transformed at 300C, fully martensitic		 5001
Isothermally transformed at 300C, fully martensitic		 5002
Isothermally transformed at 300C, fully martensitic
5003
Isothermally transformed at 300C, fully martensitic		 10002
Isothermally transformed at 300C, fully martensitic		 10001
Isothermally transformed at 300C, fully martensitic
10001
Isothermally transformed at 300C, fully martensitic		 10002
Isothermally transformed at 300C, fully martensitic		 10003
Isothermally transformed at 300C, fully martensitic
1001
Isothermally transformed at 280C for 6hr, fully martensitic		 2001
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280B-2001
Isothermally transformed at 280C for 6hr, fully martensitic
642_280B_2001
Isothermally transformed at 280C for 6hr, fully martensitic		 5007
Isothermally transformed at 280C for 6hr, fully martensitic		 5002
Isothermally transformed at 280C for 6hr, fully martensitic
5004
Isothermally transformed at 280C for 6hr, fully martensitic		 5005
Isothermally transformed at 280C for 6hr, fully martensitic		 5006
Isothermally transformed at 280C for 6hr, fully martensitic
5001
Isothermally transformed at 280C for 6hr, fully martensitic		 5003
Isothermally transformed at 280C for 6hr, fully martensitic		 5001
Isothermally transformed at 280C for 6hr, fully martensitic
5003
Isothermally transformed at 280C for 6hr, fully martensitic		 5004
Isothermally transformed at 280C for 6hr, fully martensitic		 5002
Isothermally transformed at 280C for 6hr, fully martensitic
642_280B-5002
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280B-5005
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280B-5004
Isothermally transformed at 280C for 6hr, fully martensitic
642_280B-5001
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280B-5006
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280B-5003
Isothermally transformed at 280C for 6hr, fully martensitic
642_280B_5002
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280B_5005
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280B_5003
Isothermally transformed at 280C for 6hr, fully martensitic
642_280B_5001
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280B_5004
Isothermally transformed at 280C for 6hr, fully martensitic		 10001
Isothermally transformed at 280C for 6hr, fully martensitic
10002
Isothermally transformed at 280C for 6hr, fully martensitic		 628-1
Isothermally transformed at 280C for 6hr, fully martensitic		 628-2
Isothermally transformed at 280C for 6hr, fully martensitic
628-3
Isothermally transformed at 280C for 6hr, fully martensitic		 628-4
Isothermally transformed at 280C for 6hr, fully martensitic		 628-6
Isothermally transformed at 280C for 6hr, fully martensitic
628-7
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280-1
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280-10
Isothermally transformed at 280C for 6hr, fully martensitic
642_280-11
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280-12
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280-13
Isothermally transformed at 280C for 6hr, fully martensitic
642_280-2
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280-3
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280-4
Isothermally transformed at 280C for 6hr, fully martensitic
642_280-5
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280-6
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280-7
Isothermally transformed at 280C for 6hr, fully martensitic
642_280-8
Isothermally transformed at 280C for 6hr, fully martensitic		 642_280-9
Isothermally transformed at 280C for 6hr, fully martensitic		 2002
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite
2002 anlaysis. f=0.02
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 2003_anlysis1
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 2003. f=0.04
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite
5005
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 5002
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 5003
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite
5006
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 5001
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 5004
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite
5007
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 5008
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 5009
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite
50010
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 50013
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 50016
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite
50015
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 50012
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 50014
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite
50011
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 10005
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 10003
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite
10001
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 10002
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite		 10004
Isothermally transformed at 280C for 30hr, mixture of martensite and bainite
1
Isothermally transformed at 280C for 30hr		 10
Isothermally transformed at 280C for 30hr		 11
Isothermally transformed at 280C for 30hr
12
Isothermally transformed at 280C for 30hr		 2
Isothermally transformed at 280C for 30hr		 3
Isothermally transformed at 280C for 30hr
4
Isothermally transformed at 280C for 30hr		 5
Isothermally transformed at 280C for 30hr		 6
Isothermally transformed at 280C for 30hr
7
Isothermally transformed at 280C for 30hr		 8
Isothermally transformed at 280C for 30hr		 9
Isothermally transformed at 280C for 30hr
50_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 50_01 analysis.jpg
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 100_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
100_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 100_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 100_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
100_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 200_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 200_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
200_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 200_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 200_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_03
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_04
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_05
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_05
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_04
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_03
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_07
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_09
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_08
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_14
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_10
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_11
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_06
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_15
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_16
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_23
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_27
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_06
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_24
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_20
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_08
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_25
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_07
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_16
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_21
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_19
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_26
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_18
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_04
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_12
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_28
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_10
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_22
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_13
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_17
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_11
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_09
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_14
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_15
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
500_03
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_05
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 500_29
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
1000_03
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_05
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
1000_04
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_08
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
1000_03
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_09
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
1000_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_07
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_10
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
1000_06
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_05
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_04
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
1000_03
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_02
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_01
Isothermally transformed at 280C for 7days, mixture of martensite and bainite
1000_04
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 1000_05
Isothermally transformed at 280C for 7days, mixture of martensite and bainite		 50_01
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
50_01 anlysis
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 50_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 100_05
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
100_04
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 100_03
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 100_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
100_04
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 100_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 100_03
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
100_01
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 100_06
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 100_05
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
100_09
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 100_07
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 100_08
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
200_01
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 200_05
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 200_07
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
200_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 200_04
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 200_03
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
200_06
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 200_04
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 200_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
200_03
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 200_05
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 200_01
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_11
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_10
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_13
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_01
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_15
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_14
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_03
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_09
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_05
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_08
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_12
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_06
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_07
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_04
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_07
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_08
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_10
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_04
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_03
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_01
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_12
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_10
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_14
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_05
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_16
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_03
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_06
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_13
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_09
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_12
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_07
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_08
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_04
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 500_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
500_01
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_05
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_04
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
1000_01
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_03
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
1000_06
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_01
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_04
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
1000_06
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_05
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_08
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
1000_07
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_03
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
1000_10
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_09
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_06
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
1000_05
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_02
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_04
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite
1000_01
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1000_03
Isothermally transformed at 280C for 3 weeks, mixture of martensite and bainite		 1
Isothermally transformed at 280C for 3 weeks
10
Isothermally transformed at 280C for 3 weeks		 11
Isothermally transformed at 280C for 3 weeks		 12
Isothermally transformed at 280C for 3 weeks
13
Isothermally transformed at 280C for 3 weeks		 14
Isothermally transformed at 280C for 3 weeks		 15
Isothermally transformed at 280C for 3 weeks
16
Isothermally transformed at 280C for 3 weeks		 17
Isothermally transformed at 280C for 3 weeks		 18
Isothermally transformed at 280C for 3 weeks
19
Isothermally transformed at 280C for 3 weeks		 2
Isothermally transformed at 280C for 3 weeks		 20
Isothermally transformed at 280C for 3 weeks
21
Isothermally transformed at 280C for 3 weeks		 22
Isothermally transformed at 280C for 3 weeks		 23
Isothermally transformed at 280C for 3 weeks
24
Isothermally transformed at 280C for 3 weeks		 25
Isothermally transformed at 280C for 3 weeks		 26
Isothermally transformed at 280C for 3 weeks
3
Isothermally transformed at 280C for 3 weeks		 4
Isothermally transformed at 280C for 3 weeks		 5
Isothermally transformed at 280C for 3 weeks
6
Isothermally transformed at 280C for 3 weeks		 7
Isothermally transformed at 280C for 3 weeks		 8
Isothermally transformed at 280C for 3 weeks
9
Isothermally transformed at 280C for 3 weeks		 50
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 100
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite
200(2)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 200
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 500(4)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite
500
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 500(3)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 500(2)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite
500(5)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 500(6)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 500(7)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite
1000(5)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 1000(9)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 1000(7)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite
1000(8)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 1000(2)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 1000(3)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite
1000(4)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 1000
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite		 1000(6)
Isothermally transformed at 280C for 9 weeks, mixture of martensite and bainite
6
Isothermally transformed at 280C for 9 weeks		 3
Isothermally transformed at 280C for 9 weeks		 2
Isothermally transformed at 280C for 9 weeks
4
Isothermally transformed at 280C for 9 weeks		 8
Isothermally transformed at 280C for 9 weeks		 5
Isothermally transformed at 280C for 9 weeks
7
Isothermally transformed at 280C for 9 weeks		 50_01
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite		 100_01
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite
200_01
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite		 500_02
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite		 500_01
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite
500_04
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite		 500_03
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite		 1000_02
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite
1000_05
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite		 1000_01
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite		 1000_03
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite
1000_04
Isothermally transformed at 280C for 12 weeks, mixture of martensite and bainite		 1
Isothermally transformed at 280C for 12 weeks		 10
Isothermally transformed at 280C for 12 weeks
2
Isothermally transformed at 280C for 12 weeks		 3
Isothermally transformed at 280C for 12 weeks		 4
Isothermally transformed at 280C for 12 weeks
5
Isothermally transformed at 280C for 12 weeks		 6
Isothermally transformed at 280C for 12 weeks		 7
Isothermally transformed at 280C for 12 weeks
8
Isothermally transformed at 280C for 12 weeks		 9
Isothermally transformed at 280C for 12 weeks		 1
Isothermally transformed at 280C for 12 weeks
10
Isothermally transformed at 280C for 12 weeks		 11
Isothermally transformed at 280C for 12 weeks		 12
Isothermally transformed at 280C for 12 weeks
13
Isothermally transformed at 280C for 12 weeks		 14
Isothermally transformed at 280C for 12 weeks		 15
Isothermally transformed at 280C for 12 weeks
16
Isothermally transformed at 280C for 12 weeks		 17
Isothermally transformed at 280C for 12 weeks		 18
Isothermally transformed at 280C for 12 weeks
19
Isothermally transformed at 280C for 12 weeks		 2
Isothermally transformed at 280C for 12 weeks		 20
Isothermally transformed at 280C for 12 weeks
21
Isothermally transformed at 280C for 12 weeks		 22
Isothermally transformed at 280C for 12 weeks		 23
Isothermally transformed at 280C for 12 weeks
24
Isothermally transformed at 280C for 12 weeks		 3
Isothermally transformed at 280C for 12 weeks		 4
Isothermally transformed at 280C for 12 weeks
5
Isothermally transformed at 280C for 12 weeks		 6
Isothermally transformed at 280C for 12 weeks		 7
Isothermally transformed at 280C for 12 weeks
8
Isothermally transformed at 280C for 12 weeks		 9
Isothermally transformed at 280C for 12 weeks		 100
Isothermally transformed at 260C, fully martensitic
633_260B_1001
Isothermally transformed at 260C, fully martensitic		 200
Isothermally transformed at 260C, fully martensitic		 633_260B_2001
Isothermally transformed at 260C, fully martensitic
500
Isothermally transformed at 260C, fully martensitic		 500 (3)
Isothermally transformed at 260C, fully martensitic		 500 (2)
Isothermally transformed at 260C, fully martensitic
500 (4)
Isothermally transformed at 260C, fully martensitic		 633_260B_5003
Isothermally transformed at 260C, fully martensitic		 633_260B_5001
Isothermally transformed at 260C, fully martensitic
633_260B_5002
Isothermally transformed at 260C, fully martensitic		 1000 (10)
Isothermally transformed at 260C, fully martensitic		 1000 (6)
Isothermally transformed at 260C, fully martensitic
1000 (9)
Isothermally transformed at 260C, fully martensitic		 1000
Isothermally transformed at 260C, fully martensitic		 1000 (11)
Isothermally transformed at 260C, fully martensitic
1000 (8)
Isothermally transformed at 260C, fully martensitic		 1000 (12)
Isothermally transformed at 260C, fully martensitic		 1000 (7)
Isothermally transformed at 260C, fully martensitic
633_260B_10001
Isothermally transformed at 260C, fully martensitic





δ-TRIP Stabilisation Intervention Texture Type IV
Coalesced Eutectoid Flangeability Dilatometry Bessemer
Topology Hatfield Nanostructured Cracking


Superalloys Titanium Bainite Martensite Widmanstätten ferrite
Cast iron Welding Allotriomorphic ferrite Movies Slides
Neural Networks Creep Mechanicallly Alloyed Theses Retained Austenite
Stainless Steels Nanostructured Hydroforming Diffusion Bonding TRIP



CML Home